Anti-static nylon panels to the MC nylon substrate, added carbon Department of filler to increase the conductivity performance / antistatic performance. 
 Feature 
 MC501CD filler dispersed uniform, any part of the resistance 
 The values ??are the same, after machining can be assured. 
 The inherent resistance of the volume of R2 102 to 104, R6 106 ~ 108Ω · cm 
 The R9 volume of the inherent resistance of 108 ~~ to 1010, R11, 1010 ~ 1012Ω · cm 
 R11 did not fill the timber (toner), additives and other pollution caused by 
 Less. No toner off caused by the ultra-fine particles. Is self- 
 Natural color (primary color), the appearance of clean, wide range of uses. 
 Color: black, natural color (primary color) 
 Applications: trays, rails, shielding plate, and test fixture. 
 Technical Specifications 
 Project ASTM units MC501CDR2 MC501CDR6 MC501CDR9 MC500ASR11 
 The proportion of D-792 1.20 1.23 1.19 1.15 
 Tensile strength of the D-638 Mpa 68 74 88 52 
 Elongation D-638% 10 7 12 162 
 Tensile modulus D-638 Mpa 
 Compression strength (yield point) the D-695 MPa 
 Compressive Strength (5% distortion) D-695 Mpa 98 93 33 
 Compression modulus D-695 Mpa 4210 4020 1314 
 Impact test strength (notch) D-256 J / M 35 35 35 180 
 Tortuous strength of D-790 Mpa 117 117 132 45 
 Tortuous elastic rate of D-790 Mpa 4110 4020 4.16 thousand 1216 
 ROCKWELL hardness D-785 R scale 11,911,711,993 
 Continuous use temperature ° C 120 120 150 105 
 Water Absorption (23 ° C, 24 hours in water infiltration bubble) D-570% 1.6 
 Water absorption (23 ℃, water saturated) D-570% 
 Linear expansion coefficient of the D-696 X10-5 / ° C 8.0 7.5 8.6 11.0 
 Weight to withstand temperature 1.820MPa (18.6kgf/cm2) D-648 ° C 200 200 200 75 
 0.445MPa (4.6kgf/cm2) D-648 ℃ 215 215 150 
 Volume inherent resistance to D-257 Ω · cm 102 ~ 104 106 ~ 108 108 ~ 1010 1010 ~ 1012 

 Origin: Japan